Influence of Texture and Environmental Effects on Fatigue Behavior of Ti-6Al-4V Alloy

Ti-6Al-4V alloy in solutionized and aged condition was subjected to axial fatigue testing in air and corrosive environments respectively. Severity of the methanol damage as evidenced through fractographic studies, corroborates loss in fatigue strength of samples tested in methanol environment in contrast to samples tested in air. Samples subjected to fatigue loading in NaCl environment revealed extensive secondary cracks along alpha grain boundaries.